Sintered body and high-frequency circuit component

ABSTRACT

There is provided a sintered body at least 80% of which is constituted of a Y-type hexagonal ferrite. The sintered body contains, as main components, a cobalt oxide, a copper oxide, an iron oxide and AO (AO is at least one of BaO or SrO) in predetermined amounts in mol %, more preferably contains MO (MO is at least one of NiO, ZnO or MgO) in a predetermined amount in mol % in addition to the above components, and also contains, as additional components, bismuth oxide (Bi 2 O 3 ), borosilicate glass, borosilicate zinc glass or bismuth glass in predetermined amounts in wt %. Thus, a sintered body which exhibits good magnetic properties and is usable up to a high frequency band ranging from several hundred megahertz to gigahertz, contains as few hetero phases other than a Y-type hexagonal ferrite as possible and can be calcined at a temperature of not higher than 1,000° C., particularly about 900° C., and a high-frequency circuit component using the sintered body can be provided.

TECHNICAL FIELD

[0001] The present invention relates to a sintered body used in a high-frequency circuit component and a high-frequency circuit component using the sintered body.

BACKGROUND ART

[0002] (1) In recent years, along with a size reduction in electronic equipment and a movement toward higher-frequency electronic equipment, demand for an electronic part having a high inductance and a high impedance in a high-frequency band has been increasing. To obtain a compact electronic part having a high inductance and a high impedance, it is desirable to prepare a coil having the multilayer structure that a conductive body is incorporated into a magnetic material by a so-called printing method or sheeting method.

[0003] The number of turns of the coil can be increased due to the multilayer structure and the structure is a closed magnetic circuit, so that a high inductance and a high impedance can be obtained.

[0004] As a conductive body to be incorporated into a sintered body, in general, silver (Ag) is often used in consideration of electric resistivity, a melting point and costs. Since the melting point of silver is not higher than 1,000° C., an NiZn-based ferrite which exhibits a high sintered density even when based at 900° C. has heretofore been generally used as a magnetic material for the multilayer structure.

[0005] However, since the NiZn-based ferrite has low magnetic anisotropy, it causes natural resonance at frequencies of several hundred megahertz, so that it cannot be used within a frequency band of gigahertz.

[0006] Although an air-core coil using a non-magnetic material is sometimes used as a high-frequency specification, use of the non-magnetic material makes it difficult to obtain a high inductance and a high impedance.

[0007] Meanwhile, a hexagonal ferrite hardly causes natural resonance and has high permeability even within a frequency band of gigahertz since the magnetic anisotropy in the in-plane direction of a hexagonal plate crystal is different from that in the direction perpendicular to the in-plane direction. However, in the case of the hexagonal ferrite, the firing temperature must be high in order to obtain desired sintered density and magnetic properties.

[0008] Although it has heretofore been attempted to sinter a hexagonal ferrite at a temperature lower than or equal to the melting point of Ag by using a low-melting-point oxide in the hexagonal ferrite, the yield of soft magnetic phase is low, and it is difficult to cause the magnetic properties of the hexagonal ferrite to be fully exhibited.

[0009] One of the prior arts related and similar to the present invention is Japanese Patent Application Laid-Open No. 167703-1997. In the gazette, a study is made with a particular emphasis on a Z-type hexagonal ferrite (Ba, Sr, Pb)₃(Co_(1-x)Cu_(x))₂Fe₂₄O₄₂, and V₂O₅, CuO, Bi₂O₃, MoO₃, WO₃ and PbO are added to attempt firing at low temperatures.

[0010] Further, in the gazette, reports are made on firing of a hexagonal ferrite whose primary phase is an M-type, Y-type, W-type, X-type or U-type. Particularly, in the case of a hexagonal ferrite with a Y-type primary phase which is disclosed in a specific example, that is, (Ba)₂(Co_(1-x)Cu_(x))₂Fel₁₂O₂₂, the proportion of Y-type hexagonal ferrite is not described and unknown, but since its calcination temperature is as extremely low as 700° C., its proportion is as high as about 50%, or lower when additives are added, so that it can be said that the proportion does not exceed 80% unlike the present invention. Therefore, obtained magnetic properties are not satisfactory at all. That is, although the compositions and the addition of the substances in the gazette make low-temperature firing possible, the calcination temperature is not studied sufficiently, and the magnetic properties after firing cannot be fully exhibited due to a low yield of soft magnetic phase after sintering. It can be said that this causes the problem that a high inductance and a high impedance cannot be obtained easily.

[0011] In addition, the content of CuO in the gazette is lower than that in the present invention, and there exists the problem that even if the effect of additives is considered, high properties cannot be obtained by increasing the yield of the Y-type hexagonal ferrite by firing about 900° C.

[0012] (2) In addition to the problems described in the above (1), there still exist the following problems to be solved. That is, the electric resistivity of a conventional, so-called Y-type hexagonal ferrite is as high as about 1×10⁵ Ω·m at the highest, while the electric resistivity of a Y-type hexagonal ferrite substituted with Cu or Zn for the purpose of obtaining high properties is about 1×10⁴ Ω·m, and it cannot but be said that these values are lower than the values exceeding an electric resistivity of 1×10⁵ Ω·m which is required for materials for electronic parts.

[0013] Further, since a hexagonal ferrite has a higher dielectric constant than a spinel-type ferrite, parasitic capacitance occurring in an inductor becomes large, so that the inductor is liable to cause self-resonance and an inductance and an impedance are lowered.

[0014] (3) Even if the problems described in the above (1) are solved to some degree, a further improvement in magnetic properties or the like, particularly a further improvement in permeability within a high-frequency band, is desired in the technical field associated with the present application.

[0015] By further improving the permeability within a high-frequency band, a higher inductance can be obtained (i) when the hexagonal ferrite is used as an inductance part, and higher impedance properties can be obtained (ii) when the hexagonal ferrite is used as a noise filter part.

[0016] (4) In addition to the problem described in the above (3), there still exist the following problems to be solved. That is, the electric resistivity of a conventional, so-called Y-type hexagonal ferrite is as high as about 1×10⁵ Ω·m at the highest while the electric resistivity of a Y-type hexagonal ferrite substituted with Cu or Zn for the purpose of obtaining high properties is about 1×104 Ω·m, and it cannot but be said that these values are lower than the values exceeding an electric resistivity of 1×10⁵ Ω·m which is required for materials for electronic parts.

[0017] Further, since a hexagonal ferrite has a higher dielectric constant than a spinel-type ferrite, parasitic capacitance occurring in an inductor becomes large, so that the inductor is liable to cause self-resonance and an inductance and an impedance are lowered.

DISCLOSURE OF THE INVENTION

[0018] The present invention has been invented to solve the above problems of the prior art. That is, the invention of a first group of the present invention has been invented for solving the problem of the prior art which has been described in the above (1). An object thereof is to provide a sintered body which exhibits good magnetic properties and is usable up to a high frequency band ranging from several hundred megahertz to gigahertz, contains as few hetero phases other than a Y-type hexagonal ferrite as possible and can be calcined at a temperature of not higher than 1,000° C., particularly about 900° C., and a high-frequency circuit component using the sintered body. To solve such a problem, the present invention is a sintered body at least 80% of which is constituted of a Y-type hexagonal ferrite, wherein the sintered body contains, as main components, a cobalt oxide in an amount of 3 to 15 mol % in terms of CoO, a copper oxide in an amount of 5.5 to 17 mol % in terms of CuO, an iron oxide in an amount of 57 to 61 mol % in terms of Fe₂O₃ and AO (AO is at least one of BaO or SrO) as the balance, and also contains, as an additional component, 0.5 to 7 wt % of bismuth oxide (Bi₂O₃). Further, the present invention is a high-frequency circuit component having the structure that a conductive body is embedded in a sintered body, wherein a Y-type hexagonal ferrite constitutes at least 80% of the sintered body, and the sintered magnetic oxide contains, as main components, a cobalt oxide in an amount of 3 to 15 mol % in terms of CoO, a copper oxide in an amount of 5.5 to 17 mol % in terms of CuO, an iron oxide in an amount of 57 to 61 mol % in terms of Fe₂O₃ and AO (AO is at least one of BaO or SrO) as the balance, and also contains, as an additional component, 0.5 to 7 wt % of bismuth oxide (Bi₂O₃).

[0019] The invention of a second group of the present invention has been invented for solving the problem of the prior art which has been described in the above (2). An object thereof is to provide a sintered body which can be calcined at a temperature of not higher than 1,000° C., particularly about 900° C., has high electric resistivity and a low dielectric constant and contains a Y-type hexagonal ferrite as a main ferrite component and a high-frequency circuit component using the sintered body. To solve such a problem, the present invention is a sintered body at least 80% of which is constituted of a Y-type hexagonal ferrite, wherein the sintered body contains, as main components, a cobalt oxide in an amount of 3 to 15 mol % in terms of CoO, a copper oxide in an amount of 5 to 17 mol % in terms of CuO, an iron oxide in an amount of 57 to 61 mol % in terms of Fe₂O₃ and AO (AO is at least one of BaO or SrO) as the balance and also contains, as an additional component, 0.6 to 7 wt % of borosilicate glass, borosilicate zinc glass or bismuth glass. Further, the present invention is a high-frequency circuit component having the structure that a conductive body is embedded in a sintered body, wherein a Y-type hexagonal ferrite constitutes at least 80% of the sintered body, and the sintered body contains, as main components, a cobalt oxide in an amount of 3 to 15 mol % in terms of CoO, a copper oxide in an amount of 5 to 17 mol % in terms of CuO, an iron oxide in an amount of 57 to 61 mol % in terms of Fe₂O₃ and AO (AO is at least one of BaO or SrO) as the balance and also contains, as an additional component, 0.6 to 7 wt % of borosilicate glass, borosilicate zinc glass or bismuth glass.

[0020] The invention of a third group of the present invention has been invented for solving the problem of the prior art which has been described in the above (3). An object thereof is to provide a sintered body which exhibits extremely good permeability up to a high frequency band ranging from several hundred megahertz to gigahertz, contains as few hetero phases other than a Y-type hexagonal ferrite as possible and can be calcined at a temperature of not higher than 1,000° C., particularly about 900° C., and a high-frequency circuit component using the sintered body. To solve such a problem, the present invention is a sintered body at least 80% of which is constituted of a Y-type hexagonal ferrite, wherein the sintered body contains, as main components, a cobalt oxide in an amount of 3 to 15 mol % in terms of CoO, a copper oxide in an amount of 5 to 17 mol % in terms of CuO, an iron oxide in an amount of 57 to 61 mol % in terms of Fe₂O₃, 0 to 15 wt % of MO (MO is at least one of NiO, ZnO or MgO, the content of MO would never be 0), the balance being AO (AO is at least one of BaO or SrO), and also contains, as an additional component, 0.5 to 7 wt % of bismuth oxide (Bi₂O₃). Further, the present invention is a high-frequency circuit component having the structure that a conductive body is embedded in a sintered body, wherein a Y-type hexagonal ferrite constitutes at least 80% of the sintered body, and the sintered body contains, as main components, a cobalt oxide in an amount of 3 to 15 mol % in terms of CoO, a copper oxide in an amount of 5 to 17 mol % in terms of CuO, an iron oxide in an amount of 57 to 61 mol % in terms of Fe₂O₃, 0 to 15 wt % of MO (MO is at least one of NiO, ZnO or MgO, the content of MO would never be 0), and AO (AO is at least one of BaO or SrO) as the balance, and also contains, as an additional component, 0.5 to 7 wt % of bismuth oxide (Bi₂O₃).

[0021] The invention of a fourth group of the present invention has been invented for solving the problem of the prior art which has been described in the above (4). An object thereof is to provide a sintered body which can be calcined at a temperature of not higher than 1,000° C., particularly about 900° C., has good permeability in a high-frequency band, high electric resistivity and a low dielectric constant and contains a Y-type hexagonal ferrite as a main ferrite component and a high-frequency circuit component using the sintered body. To solve such a problem, the present invention is a sintered body at least 80% of which is constituted of a Y-type hexagonal ferrite, wherein the sintered body contains, as main components, a cobalt oxide in an amount of 3 to 15 mol % in terms of CoO, a copper oxide in an amount of 5 to 17 mol % in terms of CuO, an iron oxide in an amount of 57 to 61 mol % in terms of Fe₂O₃, 0 to 15 wt % of MO (MO is at least one of NiO, ZnO or MgO, the content of MO would never be 0), and AO (AO is at least one of BaO or SrO) as the balance, and also contains, as an additional component, 0.6 to 7 wt % of borosilicate glass, borosilicate zinc glass or bismuth glass. Further, the present invention is a high-frequency circuit component having the structure that a conductive body is embedded in a sintered body, wherein the sintered body contains, as main components, a cobalt oxide in an amount of 3 to 15 mol % in terms of CoO, a copper oxide in an amount of 5 to 17 mol % in terms of CuO, an iron oxide in an amount of 57 to 61 mol % in terms of Fe₂O₃, 0 to 15 wt % of MO (MO is at least one of NiO, ZnO or MgO, the content of MO would never be 0), an AO (AO is at least one of BaO or SrO) as the balance, and also contains, as an additional component, 0.6 to 7 wt % of borosilicate glass, borosilicate zinc glass or bismuth glass.

BRIEF DESCRIPTION OF THE DRAWINGS

[0022]FIG. 1 is a schematic diagram of the inductor used in Examples.

BEST MODE OF EMBODYING THE INVENTION

[0023] A detailed description will be given to the sintered body of the present invention hereinafter.

(1) Description of The First Invention Group

[0024] Since the sintered body in the first invention group of the present invention is sintered body, it can be produced by a general ceramic production process.

[0025] The sintered body in the first invention group of the present invention contains, as main components, a cobalt oxide in an amount of 3 to 15 mol % (preferably 5 to 10 mol %) in terms of CoO, a copper oxide in an amount of 5.5 to 17 mol % (preferably 10 to 15 mol %) in terms of CuO, an iron oxide in an amount of 57 to 61 mol % (preferably 59 to 60 mol %) in terms of Fe₂O₃, and AO (AO is at least one of BaO or SrO) as the balance. The AO may be BaO, SrO or a mixture thereof.

[0026] Further, the sintered body of the present invention also contains 0.5 to 7 wt % (preferably 0.6 to 5 wt %) of bismuth oxide (Bi₂O₃) as an additional component.

[0027] As is understood from Examples to be described later, the bismuth oxide (Bi₂O₃) is added in the form of the oxide and generally remains in the form of the oxide even after sintering.

[0028] As for the contents of the above main components, when the content of CoO is lower than 3 mol %, the inconvenience that permeability at 2 GHz decreases (for example, to a value less than 2.0) is liable to occur, while when the content of CoO is higher than 15 mol %, the inconvenience that permeability at 500 MHz decreases (for example, to a value less than 2.0) is liable to occur.

[0029] Further, when the content of CuO is lower than 5.5 mol %, the inconvenience that the calcination temperature exceeds 1,000° C. is liable to occur, while when the content of CuO is higher than 17 mol %, the inconvenience that permeability decreases (for example, to a value less than 2.0) is liable to occur.

[0030] Further, when the content of Fe₂O₃ is lower than 57 mol % or higher than 61 mol %, the inconvenience that permeability decreases is liable to occur.

[0031] As for the content of the above additional component, when the content of the above Bi₂O₃ is lower than 0.5 wt %, the inconvenience that at least 90% of theoretical density cannot be obtained by firing at a temperature of not higher than 1,000° C. is liable to occur, while when the content of the above Bi₂ 0 ₃ is higher than 7 wt %, the inconvenience that permeability decreases is liable to occur.

[0032] The addition of such an additional component as Bi₂O₃, particularly together with the inclusion of the above CuO, markedly accomplishes low-temperature sintering. They also cause such a synergistic effect as an improvement in magnetic properties. When the firing temperature is lowered, an electrode-incorporated closed magnetic circuit component can be produced easily by firing the sintered magnetic oxide with a low-melting-point electrode material such as Ag which is inexpensive and has a low electrical resistance incorporated therein. The thus-produced component is used in a high-frequency component (high-frequency circuit component) such as an inductor which is compact and has a high Q value or a noise filter which is compact and exhibits a high,impedance at a particular frequency in a high-frequency band.

[0033] In addition, at least 80%, particularly preferably at least 90%, of the sintered body in the present invention is constituted of a Y-type hexagonal ferrite. The unit “%” as used herein is calculated from the ratio of main peaks of X-ray diffraction intensity.

[0034] When the proportion of the Y-type hexagonal ferrite is lower than 80%, the inconvenience that high permeability cannot be obtained at high frequencies occurs, thereby making it difficult to obtain a high-frequency circuit component having a high inductance and a high impedance.

[0035] When the sintered body is sintered together with a low-melting-point metal such as silver (Ag), the firing temperature is lowered. Therefore, the Y-type hexagonal ferrite must be produced in a proportion of at least 80% at the time of calcination so that the proportion of the Y-type hexagonal ferrite after sintering should be at least 80%. Although depending on the composition, the decomposition of BaFe₁₂O₁₉ and BaFe₂O₄ starts at about 850° C. to begin the production of the Y-type hexagonal ferrite.

[0036] However, when the decompositions of BaFe₁₂O₁₉ and BaFe₂O₄ do not proceed sufficiently, the production of the Y-type hexagonal ferrite does not proceed. Therefore, to have at least 80% of the Y-type hexagonal ferrite, the calcination temperature must be at least 850° C., particularly 850 to 1,000° C. Further, CuO must be contained in an amount of 5.5 to 17 mol %. When the calcination temperature is lower than 850° C. or the amount of CuO is out of the above range, it is difficult to produce the Y-type hexagonal ferrite in a proportion of higher than 80%. Meanwhile, when the calcination temperature is much higher than 1,000° C., fine milled powders cannot be obtained. The preparation of the fine milled powders is an extremely important technique in low-temperature firing.

[0037] From these standpoints, to achieve a high yield of the Y-type hexagonal ferrite at calcination temperatures of 850 to 1,000° C. as described above, CuO as a main component must be contained in an amount of 5.5 to 17 mol %.

[0038] The sintered body of the present invention is used as a high-frequency circuit component having the structure that a conductive body is embedded in the sintered body, such as an impeder or an inductor.

[0039] The present invention will be described in more detail with reference to Examples hereinafter.

EXPERIMENT 1-I Preparations of Example Samples and Comparative Example Samples

[0040] Each material was weighed so that the compositions of ferrites after sintering should become those shown in the following Table 1, and the materials were wet-blended in a steel ball mill for 15 hours. Then, these mixed powders were calcined in the air at the temperatures shown in Table 1 for 2 hours. Then, after predetermined amounts of Bi₂O₃ as an additional component were added as shown in Table 1, the calcined materials were milled in a steel ball mill for 15 hours.

[0041] The thus-obtained hexagonal ferrite powders were granulated and formed into desired shapes at a pressure of 100 MPa.

[0042] These green compacts were sintered at the firing temperatures shown in Table 1 for 2 hours. The compositions of the sintered hexagonal ferrites are as shown in the following Table 1. These samples were measured for density and magnetic permeabilities at frequencies of 500 MHz and 2 GHz at 25° C., and the results of the measurements are shown in Table 1. The target magnetic permeabilities at frequencies of 500 MHz and 2 GHz each are a value of at least 2.0.

[0043] In addition, the proportion of a Y-type hexagonal ferrite was calculated from the ratio of intensities of X-ray diffraction peaks using the milled powders of the sintered body. TABLE 1 Additional Main Components Component Calcination Firing Proportion (mol %) (wt %) Temperature Temperature of Y-Type Density Permeability Sample No. Fe₂O₃ CoO CuO BaO SrO Bi₂O₃ (° C.) (° C.) (%) (Mg/m³) 500 MHz 2 GHz Example 1 60 15 5.5 19.5 — 5 1000 930 95 5.2 2.1 2.1 Example 2 60 10 10 20 — 5 950 930 95 5.3 2.6 2.6 Example 3 60 3 17 20 — 5 950 930 95 5.3 3.0 2.8 Example 4 57 15 5.5 22.5 — 5 1000 930 95 5.2 2.0 2.0 Example 5 61 14.5 5.5 19 — 5 1000 930 95 5.2 2.0 2.0 Example 6 60 5 15 10 10 5 950 930 95 5.3 3.2 3.2 Comparative 60 17 3 20 — 5 1100 930 95 5.0 1.8 1.8 Example 1 Comparative 60 2 18 20 — 5 950 930 95 5.3 2.5 1.8 Example 2 Comparative 56 15 5 24 — 5 1000 930 73 5.2 1.9 1.9 Example 3 Comparative 62 15 5 20 — 5 1000 930 77 5.2 1.9 1.9 Example 4 Example 7 60 5 15 20 — 0.5 950 930 100 5.2 3.7 3.7 Comparative 60 5 15 20 — 0.1 950 930 100 4.8 3.5 3.5 Example 5 Example 8 60 15 5.5 19.5 — 7 1000 930 90 5.3 2.0 2.0 Comparative 60 15 5.5 19.5 — 10 1000 930 85 5.5 1.9 1.9 Example 6 Example 9 60 15 5.5 19.5 — 5 900 930 83 5.0 2.0 2.0 Example 10 60 5 15 20 — 5 850 930 90 5.0 3.2 3.2 Comparative 60 15 5.5 19.5 — 5 850 930 46 4.7 1.8 1.8 Example 7 Comparative 60 15 5.5 19.5 — 5 800 930 40 4.7 1.5 1.5 Example 8 Comparative 60 15 5 20 — 1 700 930 30 4.5 1.5 1.5 Example 9

EXPERIMENT 1-II

[0044] Then, an impeder was prepared using the magnetic body of the present invention. That is, each material was weighed so that the composition after sintering should become the composition of the sample of Example 7 in the above Table 1, and the materials were wet-blended in a steel ball mill for 15 hours. Then, these mixed powders were calcined in the air at 950° C. for 2 hours. Then, after 5 wt % of Bi₂O₃ was added as an additional component, the calcined powders were milled in a steel ball mill for 15 hours.

[0045] An organic binder was mixed into the calcined powders, and the paste was formed into a uniform green sheet by a doctor blade process.

[0046] For comparison, another green sheet was prepared using NiCuZn-based spinel ferrite powders (NiO=45 mol %, CuO=5 mol %, ZnO=1.5 mol %, Fe₂O₃=48 mol %, CoO =0.5 mol %).

[0047] Meanwhile, a conductive paste containing silver was prepared, and a coil was stacked in a spiral form on the above green sheet. A pressure was applied in the thickness direction to crimp the coil onto the sheet, thereby preparing a stacked green sheet having the electrode sandwiched between the magnetic bodies. In this way the prepared green chip was sintered at 930° C. for 2 hours. The silver paste was applied to the sides of the internal conductor of the obtained sintered body to bake external electrodes thereto, thereby obtaining an impeder (high-frequency circuit component) whose schematic constitution is shown in FIG. 1. FIG. 1 shows the impeder schematically for the purpose of facilitating understanding of the internal structure thereof. In FIG. 1, reference numeral 11 denotes an inner conductor (Ag coil), reference numeral 10 terminal conductors, and reference numeral 20 a ferrite.

[0048] When the impedance and permeability of the thus-obtained impeder were measured at a frequency of 2 GHz, the impedance of the conventional NiCuZn-based spinel ferrite was 135 Ω (permeability: 1.2), while the impedance of the magnetic body of the present invention was 208 Ω (permeability: 3.7) with the result of an improvement of about 54% or higher over the conventional ferrite.

[0049] The effect of the first invention group of the present invention is obvious from the above result. That is, the present invention is a sintered body at least 80% of which is constituted of a Y-type hexagonal ferrite, wherein the sintered magnetic oxide contains, as main components, a cobalt oxide in an amount of 3 to 15 mol % in terms of CoO, a copper oxide in an amount of 5.5 to 17 mol % in terms of CuO, an iron oxide in an amount of 57 to 61 mol % in terms of Fe₂O₃, and AO (AO is at least one of BaO or SrO) as the balance, and also contains, as an additional component, 0.5 to 7 wt % of bismuth oxide (Bi₂O₃). Thus, a sintered body which exhibits good magnetic properties and is usable up to a high frequency band ranging from several hundred megahertz to gigahertz, contains as few hetero phases other than a Y-type hexagonal ferrite as possible and can be calcined at a temperature of not higher than 1,000° C., particularly about 900° C., and a high-frequency circuit component using the sintered body can be provided.

(2) Description of The Second Invention Group

[0050] Since the sintered body in the second invention group of the present invention is sintered body, it can be produced by a general ceramic production process.

[0051] The sintered body in the second invention group of the present invention contains, as main components, a cobalt oxide in an amount of 3 to 15 mol % (preferably 3 to 5 mol %) in terms of CoO, a copper oxide in an amount of 5 to 17 mol % (preferably 5.5 to 10 mol %) in terms of CuO, an iron oxide in an amount of 57 to 61 mol % (preferably 59 to 60 mol %) in terms of Fe₂O₃, and AO (AO is at least one of BaO or SrO) as the balance. The AO may be BaO, SrO or a mixture thereof.

[0052] Further, the sintered body of the present invention also contains 0.6 to 7 wt % (preferably 0.6 to 5 wt %) of borosilicate glass, borosilicate zinc glass or bismuth glass as an additional component.

[0053] The borosilicate glass generally indicates glass containing B₂O₃ and SiO₂, the borosilicate zinc glass generally indicates glass containing B₂O₃, SiO₂ and ZnO, and the bismuth glass generally indicates glass containing Bi₂O₃. In the definitions of these glasses, the above components do not need to be main components.

[0054] These additional glass components may be used solely or in admixture of two or three. When they are used in admixture of two or three, the total wt % of the mixture should be within the above range.

[0055] By the addition of such glass, an increase in electric resistivity (increasing electric resistivity) or a decrease in dielectric constant (decreasing a dielectric constant) can be achieved. Therefore, by the addition of the glass specified by the present invention, an electric resistivity of at least 1×10⁵ Ω·m which is required for, for example, a multilayer component material as a high-frequency circuit component. Further, by the addition of the glass specified by the present invention, the effect of decreasing a dielectric constant is also exhibited, and when the sintered body of the present invention is used as a high-frequency component, a high impedance can be attained at high frequencies and the frequency band for the impedance can be widened.

[0056] Further, the above glasses must be added in the form of glass. After firing, the glass component used remains in the sintered body regardless of whether the component maintains the glass form.

[0057] Of these glasses, borosilicate glass and borosilicate zinc glass are particularly preferable for achieving high electric resistivity and a low dielectric constant more effectively. Further, when the above glasses are added in the same amount, bismuth glass is particularly preferable from the viewpoint that the temperature at which a relative density of at least 90% can be attained can be lowered.

[0058] As for the contents of the above main components, when the content of CoO is lower than 3 mol %, the inconvenience that permeability at 2 GHz decreases (for example, to a value less than 2.0) is liable to occur, while when the content of CoO is higher than 15 mol %, the inconvenience that permeability at 500 MHz decreases (for example, to a value less than 2.0) is liable to occur, for example.

[0059] Further, when the content of CuO is lower than 5 mol %, the inconvenience that the calcination temperature exceeds 1,000° C. is liable to occur, while when the content of CuO is higher than 17 mol %, the inconvenience that permeability decreases (for example, to a value less than 2.0) is liable to occur.

[0060] Further, when the content of Fe₂O₃ is lower than 57 mol % or higher than 61 mol %, the inconvenience that permeability decreases is liable to occur.

[0061] As for the content of the above additional component, when the content of the above specified glass is lower than 0.6 wt %, the inconvenience that at least 90% of theoretical density cannot be obtained by firing at a temperature of not higher than 1,000° C. is liable to occur, while when the content of the above glass is higher than 7 wt %, the inconvenience that permeability decreases is liable to occur.

[0062] The addition of such an additional glass component, particularly together with the inclusion of the above CuO, markedly accomplishes low-temperature sintering. When the firing temperature is lowered, an electrode-incorporated closed magnetic circuit component can be produced easily by firing the sintered body with a low-melting-point electrode material such as Ag which is inexpensive and has a low electrical resistance incorporated therein. The thus-produced component is used in a high-frequency component (high-frequency circuit component) such as an inductor which is compact and has a high Q value or a noise filter which is compact and exhibits a high impedance at a particular frequency in a high-frequency band.

[0063] In addition, at least 80%, particularly preferably at least 90%, of the sintered body in the present invention is constituted of a Y-type hexagonal ferrite. The unit “%” as used herein is calculated from the ratio of main peaks of X-ray diffraction intensity.

[0064] When the sintered body is sintered together with a low-melting-point metal such as silver (Ag), the firing temperature is lowered. Therefore, the Y-type hexagonal ferrite must be produced in a proportion of at least 80% at the time of calcination so that the proportion of the Y-type hexagonal ferrite after sintering should be at least 80%. Although varying depending on the composition, the decompositions of BaFe₁₂O₁₉ and BaFe₂O₄ start about 850° C. and the production of the Y-type hexagonal ferrite starts. However, when the decompositions of BaFe₁₂O₁₉ and BaFe₂O₄ do not proceed sufficiently, the production of the Y-type hexagonal ferrite does not proceed. Therefore, to have at least 80% of the Y-type hexagonal ferrite, the calcination temperature must be at least 850° C., particularly 850 to 1,000° C. Further, CuO must be contained in an amount of 5.5 to 17 mol %. When the calcination temperature is lower than 850° C. or a predetermined amount of CuO is not contained, it is difficult to produce the Y-type hexagonal ferrite in a proportion of higher than 80%. Meanwhile, when the calcination temperature is much higher than 1,000° C., fine milled powders cannot be obtained. The preparation of the fine milled powders is an extremely important technique in low-temperature firing.

[0065] From these standpoints, to achieve a high yield of the Y-type hexagonal ferrite at calcination temperatures of 850 to 1,000° C. as described above, CuO as a main component must be preferably contained in an amount of 5.5 to 17 mol %.

[0066] The sintered magnetic oxide of the present invention is used as a high-frequency circuit component having the structure that a conductive body is embedded in the sintered magnetic oxide, such as an impeder or an inductor.

[0067] The present invention will be described in more detail with reference to Examples hereinafter.

EXPERIMENT 2-I Preparations of Example Samples and Comparative Example Samples

[0068] Each material was weighed so that the compositions of ferrites after sintering should become those shown in the following Table 2, and the materials were wet-blended in a steel ball mill for 15 hours. Then, these mixed powders were calcined in the air at the temperatures shown in Table 2 for 2 hours. Then, after predetermined amounts of the predetermined glasses as an additional component were added as shown in Table 2, the calcined materials were milled in a steel ball mill for 15 hours.

[0069] The thus-obtained hexagonal ferrite powders were granulated and formed into desired shapes at a pressure of 100 MPa.

[0070] These green compacts were sintered at the firing temperatures shown in Table 2 for 2 hours. The compositions of the sintered hexagonal ferrites are as shown in the following Table 2. These samples were measured for magnetic permeabilities at frequencies of 500 MHz and 2 GHz at 25° C., electric resistivity and a dielectric constant, and the results of the measurements are shown in Table 2. The target magnetic permeabilities at frequencies of 500 MHz and 2 GHz each are a value of at least 2.0. Further, the target electric resistivity is a value of 1×10⁵ Ω·m. The lower the dielectric constant, the better it is. In this regard, it has been found from the experiment results to be described later that when the electric resistivity is higher than 1×10⁵ Ω·m, the dielectric constant exhibits a low value of 30 or smaller.

[0071] In addition, the proportion of a Y-type hexagonal ferrite was calculated from the ratio of intensities of X-ray diffraction peaks using the milled powders of the sintered body. TABLE 2 Additional Component (wt %) Calcin- Boro- ation Firing Propor- Permea- Electric Main Components Bis- Boro- silicate Temper- Temper- tion of bility Resist- Di- (mol %) muth silicate Zinc ature ature Y-Type 500 2 ivity electric Sample No. Fe₂O₃ CoO CuO BaO SrO Glass Glass Glass (° C.) (° C.) (%) MHz GHz (Ω · m) Constant Example 60 15 5.5 19.5 — 5 — — 1000 930 95 2.1 2.1 1 × 10⁶ 27 2-I-1 Example 60 10 10 20 — 5 — — 950 930 95 2.6 2.6 1 × 10⁶ 27 2-I-2 Example 60 3 17 20 — 5 — — 950 930 95 3.0 2.8 9 × 10⁵ 30 2-I-3 Example 57 15 5.5 22.5 — 5 — — 1000 930 95 2.0 2.0 1 × 10⁶ 27 2-I-4 Example 61 15 5.5 18.5 — 5 — — 1000 930 95 2.0 2.0 1 × 10⁶ 27 2-I-5 Example 60 5 15 10 10 5 — — 950 930 95 3.2 3.2 1 × 10⁶ 27 2-I-6 Comparative 60 20 0 20 — 5 — — 1100 930 95 1.8 1.8 1 × 10⁶ 27 Example 2-I-1 Comparative 60 2 18 20 — 5 — — 950 930 95 2.5 1.8 9 × 10⁵ 30 Example 2-I-2 Comparative 56 15 5 20 — 5 — — 1000 930 73 1.9 1.9 1 × 10⁶ 27 Example 2-I-3 Comparative 62 15 5 20 — 5 — — 1000 930 77 1.9 1.9 1 × 10⁶ 27 Example 2-I-4 Example 60 15 5.5 19.5 — 5 — — 1000 930 95 2.1 2.1 1 × 10⁶ 27 2-I-7 Example 60 15 5.5 19.5 — 5 — — 900 930 83 2.0 2.0 1 × 10⁶ 27 2-I-8 Comparative 60 15 5 20 — 5 — — 850 930 46 1.8 1.8 1 × 10⁶ 27 Example 2-I-5 Comparative 60 15 5 20 — 5 — — 800 930 0 1.5 1.5 1 × 10⁶ 27 Example 2-I-6 Comparative 60 5 15 20 — 0.3 — — 950 930 100 3.5 3.5 5 × 10⁴ 35 Example 2-I-7 Example 60 5 15 20 — 0.6 — — 950 930 100 3.7 3.7 1 × 10⁵ 30 2-I-9 Example 60 5 15 20 — 7 — — 950 930 95 2.0 2.0 2 × 10⁶ 27 2-I-10 Comparative 60 5 15 20 — 10 — — 950 930 95 1.9 1.9 3 × 10⁶ 27 Example 2-I-8 Comparative 60 5 5 20 — — 0.3 — 950 930 100 3.3 3.3 8 × 10⁴ 32 Example 2-I-9 Example 60 5 5 20 — — 0.6 — 950 930 100 3.5 3.5 1 × 10⁵ 29 2-I-11 Example 60 5 5 20 — — 5 — 950 930 95 3.1 3.1 3 × 10⁵ 25 2-I-12 Example 60 5 5 20 — — 7 — 950 930 95 2.1 2.1 9 × 10⁶ 25 2-I-13 Comparative 60 5 5 20 — — 10 — 950 930 95 2.0 1.9 2 × 10⁷ 25 Example 2-I-10 Comparative 60 5 5 20 — — — 0.3 950 930 100 3.5 3.5 8 × 10⁴ 31 Example 2-I-11 Example 60 5 5 20 — — — 0.6 950 930 100 3.7 3.7 2 × 10⁵ 28 2-I-14 Example 60 5 5 20 — — — 5 950 930 95 3.3 3.3 6 × 10⁶ 25 2-I-15 Example 60 5 5 20 — — — 7 950 930 95 2.2 2.2 3 × 10⁷ 25 2-I-16 Comparative 60 5 5 20 — — — 10 950 930 95 1.9 1.9 5 × 10⁷ 25 Example 2-I-12 Example 60 5 5 20 — 5 — — 850 930 90 3.5 3.1 9 × 10⁵ 30 2-I-17 Example 60 5 5 20 — 5 — — 950 930 95 3.3 3.3 1 × 10⁶ 27 2-I-18

EXPERIMENT 2-II

[0072] A variety of samples were prepared by varying the types and amounts of the additional components to be added to the main components of Example 2-I-6 of the above Experiment 2-I as shown in the following Table 3. These samples were measured for the temperature at which a relative density of at least 90% (based on a theoretical density of 100).

[0073] The results are shown in the following Table 3. TABLE 3 Additional Amount of Glass Added Components 0.6 wt % 1 wt % 3 wt % 5 wt % 7 wt % Borosilicate Glass 1000° C. 1000° C. 950° C. 950° C. 900° C. Borosilicate Zinc 1000° C. 1000° C. 950° C. 950° C. 900° C. Glass Bismuth Glass 1000° C.  950° C. 900° C. 900° C. 900° C.

EXPERIMENT 2-III

[0074] Then, an inductance element was prepared using the magnetic body of the present invention. That is, each material was weighed so that the composition after sintering should become the composition of the Example 2-I-6 sample in the above Table 2, and the materials were wet-blended in a steel ball mill for 15 hours. Then, these mixed powders were calcined in the air at 950° C. for 2 hours. Then, after 5 wt % of bismuth glass was added as an additional component, the calcined powders were milled in a steel ball mill for 15 hours.

[0075] An organic binder was mixed into the calcined powders, and the paste was formed into a uniform green sheet by a doctor blade process.

[0076] For comparison, another green sheet was prepared using NiZn-based spinel ferrite powders (NiO=45 mol %, CuO=5 mol %, ZnO=1.5 mol %, Fe₂O₃=48 mol %, CoO=0.5 mol %).

[0077] Meanwhile, a conductive paste containing silver was prepared, and a coil was stacked in a spiral form on the above green sheet. A pressure was applied in the thickness direction to crimp the coil onto the sheet, thereby preparing a stacked green sheet having the electrode sandwiched between the magnetic bodies. In this way the prepared green chip was sintered at 930° C. for 2 hours. The silver paste was applied to the sides of the internal conductor of the obtained sintered body to bake external electrodes thereto, thereby obtaining an impeder (high-frequency circuit component) whose schematic constitution is shown in FIG. 1. FIG. 1 shows the impeder schematically for the purpose of facilitating understanding of the internal structure thereof. In FIG. 1, reference numeral 11 denotes an inner conductor (Ag coil), reference numeral 10 terminal conductors, and reference numeral 20 a ferrite.

[0078] When the impedance and permeability of the obtained inductance element were measured at a frequency of 2 GHz, the impedance of the magnetic body of the present invention was 208 Ω (permeability: 3.7), while the impedance of the NiCuZn ferrite was 135 Ω (permeability: 1.2)

[0079] The effect of the second invention group of the present invention is obvious from the above result. That is, the present invention is a sintered body at least 80% of which is constituted of a Y-type hexagonal ferrite, wherein the sintered magnetic oxide contains, as main components, a cobalt oxide in an amount of 3 to 15 mol % in terms of CoO, a copper oxide in an amount of 5 to 17 mol % in terms of CuO, an iron oxide in an amount of 57 to 61 mol % in terms of Fe₂O₃, and AO (AO is at least one of BaO or SrO) as the balance, and also contains, as an additional component, 0.6 to 7 wt % of borosilicate glass, borosilicate zinc glass or bismuth glass. Thus, a sintered body which can be calcined at a temperature of not higher than 1,000° C., particularly about 900° C., has high electric resistivity and a low dielectric constant and contains a Y-type hexagonal ferrite as a main ferrite component and a high-frequency circuit component using the sintered body can be provided.

(3) Description of the Third Invention Group

[0080] Since the sintered body in the third invention group of the present invention is sintered body, it can be produced by a general ceramic production process.

[0081] The sintered body in the third invention group of the present invention contains, as main components, a cobalt oxide in an amount of 3 to 15 mol % (preferably 3 to 5 mol %) in terms of CoO, a copper oxide in an amount of 5 to 17 mol % (preferably 5.5 to 10 mol %) in terms of CuO, an iron oxide in an amount of 57 to 61 mol % (preferably 59 to 60 mol %) in terms of Fe₂O₃, MO (MO is at least one of NiO, ZnO or MgO, the content of MO would never be 0) in an amount of 0 to 15 wt %, preferably 1 to 15 wt %, particularly preferably 5 to 15 wt %, and AO (AO is at least one of BaO or SrO) as the balance. The MO may be NiO, ZnO, MgO or a mixture of at least two of these compounds. When a mixture of at least two of these compounds is used as the MO, the total mol % of the mixture should be within the above range. The AO may be BaO, SrO or a mixture thereof.

[0082] Further, the sintered body of the present invention also contains 0.5 to 7 wt % (preferably 0.6 to 5 wt %) of bismuth oxide (Bi₂O₃) as an additional component.

[0083] As is understood from Examples to be described later, the bismuth oxide (Bi₂O₃) is added in the form of the oxide and generally remains in the form of the oxide even after sintering.

[0084] As for the contents of the above main components, when the content of CoO is lower than 3 mol %, for example, the inconvenience that permeability at 2 GHz decreases (for example, to a value less than 2.0) is liable to occur, while when the content of CoO is higher than 15 mol %, the inconvenience that permeability at 500 MHz decreases (for example, to a value less than 2.0) is liable to occur, for example.

[0085] Further, when the content of CuO is lower than 5 mol %, the inconvenience that the calcination temperature exceeds 1,000° C. is liable to occur, while when the content of CuO is higher than 17 mol %, the inconvenience that permeability decreases (for example, to a value less than 2.0) is liable to occur.

[0086] Further, when the content of Fe₂O₃ is lower than 57 mol % or higher than 61 mol %, the inconvenience that permeability decreases is liable to occur.

[0087] As for the content of the above additional component, when the content of the above Bi₂O₃ is lower than 0.5 wt %, the inconvenience that at least 90% of theoretical density cannot be obtained by firing at a temperature of not higher than 1,000° C. is liable to occur, while when the content of the above Bi₂O₃ is higher than 7 wt %, the inconvenience that permeability decreases is liable to occur. The addition of such an additional component as Bi₂O₃, particularly together with the inclusion of the above CuO, markedly accomplishes low-temperature sintering. They also cause such a synergistic effect as an improvement in magnetic properties. When the firing temperature is lowered, an electrode-incorporated closed magnetic circuit component can be produced easily by firing the sintered magnetic oxide with a low-melting-point electrode material such as Ag which is inexpensive and has a low electrical resistance incorporated therein.

[0088] The thus-produced component is used in a high-frequency component (high-frequency circuit component) such as an inductor which is compact and has a high Q value or a noise filter which is compact and exhibits a high impedance at a particular frequency in a high-frequency band.

[0089] When ZnO is contained in an amount of 0 to 15 wt % (the content of ZnO would never be 0) as the MO, permeability can be significantly improved, and a particularly preferable effect is given to the attainment of a high impedance and broadening of the frequency band for the impedance when a high-frequency circuit component is prepared. Meanwhile, when NiO or MgO is contained in an amount of 0 to 15 wt % (the content of ZnO would never be 0) as the MO, permeability is improved and a resonance frequency is increased. Therefore, as a high-frequency circuit component, the sintered magnetic oxide of the present invention exhibits a particularly preferable effect on controlling a high impedance and the band of the impedance.

[0090] In addition, at least 80%, particularly preferably at least 90%, of the sintered body in the present invention is constituted of a Y-type hexagonal ferrite. The unit “%” as used herein is calculated from the ratio of main peaks of X-ray diffraction intensity.

[0091] When the proportion of the Y-type hexagonal ferrite is lower than 80%, the inconvenience that high permeability cannot be obtained at high frequencies occurs, whereby a high-frequency circuit component having a high inductance and a high impedance cannot be obtained easily.

[0092] When the sintered magnetic oxide is sintered together with a low-melting-point metal such as silver (Ag), the firing temperature is lowered. Therefore, the Y-type hexagonal ferrite must be produced in a proportion of at least 80% at the time of calcination so that the proportion of the Y-type hexagonal ferrite after sintering should be at least 80%. Although varying depending on the composition, the decompositions of BaFe₁₂O₁₉ and BaFe₂O₄ start about 850° C. and the production of the Y-type hexagonal ferrite starts. However, when the decompositions of BaFe₁₂O₁₉ and BaFe₂O₄ do not proceed sufficiently, the production of the Y-type hexagonal ferrite does not proceed. Therefore, to have at least 80% of the Y-type hexagonal ferrite, the calcination temperature must be at least 850° C., particularly 850 to 1,000° C. Further, CuO must be contained in an amount of preferably 5.5 to 17 mol %. When the calcination temperature is lower than 850° C. or the amount of CuO is out of the above range, it is difficult to produce the Y-type hexagonal ferrite in a proportion of higher than 80%. Meanwhile, when the calcination temperature is much higher than 1,000° C., fine milled powders cannot be obtained. The preparation of the fine milled powders is an extremely important technique in low-temperature firing.

[0093] From these standpoints, to achieve a high yield of the Y-type hexagonal ferrite at calcination temperatures of 850 to 1,000° C. as described above, CuO as a main component must be preferably contained in an amount of 5.5 to 17 mol %.

[0094] The sintered body of the present invention is used as a high-frequency circuit component having the structure that a conductive body is embedded in the sintered magnetic oxide, such as an impeder or an inductor.

[0095] The present invention will be described in more detail with reference to Examples hereinafter.

EXPERIMENT 3-I Preparations of Example Samples and Comparative Example Samples

[0096] Each material was weighed so that the compositions of ferrites after sintering should become those shown in the following Table 4, and the materials were wet-blended in a steel ball mill for 15 hours. Then, these mixed powders were calcined in the air at the temperatures shown in Table 4 for 2 hours. Then, after predetermined amounts of Bi₂O₃ as an additional component were added as shown in Table 4, the calcined materials were milled in a steel ball mill for 15 hours.

[0097] The thus-obtained hexagonal ferrite powders were granulated and formed into desired shapes at a pressure of 100 MPa.

[0098] These green compacts were sintered at the firing temperatures shown in Table 4 for 2 hours. The compositions of the sintered hexagonal ferrites are as shown in the following Table 4. These samples were measured for magnetic permeabilities at frequencies of 500 MHz and 2 GHz at 25° C., and the results of the measurements are shown in Table 4. The target permeability at a frequency of 500 MHz is a value of at least 2.5, and the target permeability at a frequency of 2 GHz is a value of at least 2.0.

[0099] In addition, the proportion of a Y-type hexagonal ferrite was calculated from the ratio of intensities of X-ray diffraction peaks using the milled powders of the sintered body. TABLE 4 Addi- tional Calci- Propor- Compo- nation Firing tion Permea- nent Temper- Temper- of bility Main Components (mol %) (wt %) ature ature Y-Type Density 500 2 Sample No. Fe₂O₃ CoO CuO ZnO NiO MgO BaO SrO Bi₂O₃ (° C.) (° C.) (%) (Mg/m³) MHz GHz Example 3-1 60 10 5.5 5 — — 19.5 — 5 1000 930 95 5.2 3.4 3.7 Example 3-2 60 5 10 5 — — 20 — 5 950 930 95 5.3 3.8 3.8 Example 3-3 60 3 17 5 — — 15 — 5 950 930 95 5.3 4.3 3.9 Example 3-4 57 10 5.5 5 — — 22.5 — 5 1000 930 95 5.1 3.0 3.0 Example 3-5 61 9.5 5.5 5 — — 19 — 5 1000 930 95 5.3 3.0 3.0 Example 3-6 60 5 15 5 — — 10 10 5 950 930 95 5.1 3.9 3.9 Comparative 60 17 3 5 — — 15 — 5 1100 930 95 5.0 1.8 1.8 Example 3-1 Comparative 60 2 13 5 — — 20 — 5 950 930 95 5.2 2.5 1.8 Example 3-2 Comparative 56 10 5 5 — — 24 — 5 1000 930 73 5.0 2.6 1.8 Example 3-3 Comparative 62 10 5 5 — — 18 — 5 1000 930 77 5.1 2.4 2.3 Example 3-4 Example 3-7 60 10 5.5 5 — — 19.5 — 5 1000 930 95 5.2 3.4 3.7 Example 3-8 60 10 5.5 5 — — 19.5 — 5 900 930 83 5.0 3.3 3.5 Comparative 60 10 5 5 — — 20 — 5 850 930 46 4.7 2.8 2.8 Example 3-5 Comparative 60 10 5 5 — — 20 — 5 800 930 0 4.7 1.8 1.8 Example 3-6 Comparative 60 15 5 — — — 20 — 1 700 930 30 4.5 1.5 1.5 Example 3-7 Example 3-9 60 3 15 2 — — 20 — 0.5 950 930 100 5.0 3.8 3.8 Comparative 60 3 15 2 — — 20 — 0.3 950 930 100 4.8 3.6 3.6 Example 3-8 Example 3-10 60 10 5.5 5 — — 19.5 — 7 1000 930 90 5.3 3.5 3.7 Comparative 60 10 5 5 — — 20 — 10 1000 930 85 5.5 3.0 1.9 Example 3-9 Example 3-11 60 5 5.5 10 — — 19.5 — 5 1000 930 95 5.2 5.1 4.2 Example 3-12 60 3 5.5 15 — — 16.5 — 5 1000 930 95 5.2 10.1 2.2 Example 3-13 60 10 5.5 — 5 — 19.5 — 5 1000 930 95 5.2 2.7 2.3 Example 3-14 60 5 5.5 — 10 — 19.5 — 5 1000 930 95 5.2 3.3 2.6 Example 3-15 60 3 5.5 — 15 — 16.5 — 5 1000 930 95 5.2 5.8 2.0 Example 3-16 60 10 5.5 — — 5 19.5 10 5 1000 930 95 5.2 2.6 2.2 Example 3-17 60 5 5.5 — — 10 19.5 — 5 1000 930 95 5.2 3.2 2.5 Example 3-18 60 3 5.5 — — 15 16.5 — 5 1000 930 95 5.2 6.2 2.0 Comparative 60 15 5 — — — — — 5 1000 930 95 5.2 2.1 2.1 Example 3-10 Comparative 60 3 5 20 — — 12 — 5 1000 930 95 5.0 8.1 0.8 Example 3-11 Comparative 60 3 5 — 20 — 12 — 5 1000 930 95 5.0 5.8 0.8 Example 3-12 Comparative 60 3 5 — — 20 12 — 5 1000 930 95 5.0 6.2 0.6 Example 3-13 Example 3-19 57 15 5.5 8 — — 14.5 — 5 1000 930 95 5.0 3.0 3.0 Example 3-20 60 5 10 5 — — 20 — 5 850 930 90 5.0 3.5 3.5

EXPERIMENT EXAMPLE 3-II

[0100] Then, an inductance element was prepared using the magnetic body of the present invention. That is, each material was weighed so that the composition after sintering should become the composition of the sample of Example 3-11 in the above Table 4, and the materials were wet-blended in a steel ball mill for 15 hours. Then, these mixed powders were calcined in the air at 950° C. for 2 hours. Then, after 5 wt % of Bi₂O₃ was added as an additional component, the calcined powders were milled in a steel ball mill for 15 hours.

[0101] An organic binder was mixed into the calcined powders, and the paste was formed into a uniform green sheet by a doctor blade process.

[0102] For comparison, another green sheet was prepared using NiCuZn-based spinel ferrite powders (NiO=45 mol %, CuO=5 mol %, ZnO=1.5 mol %, Fe₂O₃=48 mol %, CoO=0.5 mol %).

[0103] Meanwhile, a conductive paste containing silver was prepared, and a coil was stacked in a spiral form on the above green sheet. A pressure was applied in the thickness direction to crimp the coil onto the sheet, thereby preparing a stacked green sheet having the electrode sandwiched between the magnetic bodies. In this way the prepared green chip was sintered at 930° C. for 2 hours. The silver paste was applied to the sides of the internal conductor of the obtained sintered body to bake external electrodes thereto, thereby obtaining an impeder (high-frequency circuit component) whose schematic constitution is shown in FIG. 1. FIG. 1 shows the impeder schematically for the purpose of facilitating understanding of the internal structure thereof. In FIG. 1, reference numeral 11 denotes an inner conductor (Ag coil), reference numeral 10 terminal conductors, and reference numeral 20 a ferrite.

[0104] When the impedance and permeability of the obtained impeder were measured at a frequency of 2 GHz, the magnetic body of the present invention exhibited an extremely excellent impedance of 236 Ω (permeability: 4.2). On the other hand, the impedance of the conventional NiCuZn ferrite was 135 Ω (permeability: 1.2).

[0105] The effect of the third invention group of the present invention is obvious from the above result. That is, the present invention is a sintered body at least 80% of which is constituted of a Y-type hexagonal ferrite, wherein the sintered magnetic oxide contains, as main components, a cobalt oxide in an amount of 3 to 15 mol % in terms of CoO, a copper oxide in an amount of 5 to 17 mol % in terms of CuO, an iron oxide in an amount of 57 to 61 mol % in terms of Fe₂O₃, 0 to 15 wt % of MO (MO is at least one of NiO, ZnO or MgO, the content of MO would never be 0), and AO (AO is at least one of BaO or SrO) as the balance, and also contains, as an additional component, 0.5 to 7 wt % of bismuth oxide (Bi₂O₃). Thus, a sintered body which exhibits good magnetic properties up to a high frequency band ranging from several hundred megahertz to gigahertz, contains as few hetero phases other than a Y-type hexagonal ferrite as possible and can be calcined at a temperature of not higher than 1,000° C., particularly about 900° C., and a high-frequency circuit component using the sintered body can be provided.

(4) Description of The Fourth Invention Group

[0106] Since the sintered body in the fourth invention group of the present invention is sintered body, it can be produced by a general ceramic production process.

[0107] The sintered body in the fourth invention group of the present invention contains, as main components, a cobalt oxide in an amount of 3 to 15 mol % (preferably 3 to 5 mol %) in terms of CoO, a copper oxide in an amount of 5 to 17 mol % (preferably 5.5 to 10 mol %) in terms of CuO, an iron oxide in an amount of 57 to 61 mol % (preferably 59 to 60 mol %) in terms of Fe₂O₃, MO (MO is at least one of NiO, ZnO or MgO, the content of MO would never be 0) in an amount of 0 to 15 wt %, preferably 1 to 15 wt %, particularly preferably 5 to 15 wt %, and AO (AO is at least one of BaO or SrO) as the balance.

[0108] The MO may be NiO, ZnO, MgO or a mixture of at least two of these compounds. When a mixture of at least two of these compounds is used, the total mol % of the mixture should be within the above range.

[0109] The AO may be BaO, SrO or a mixture thereof.

[0110] Further, the sintered body of the present invention also contains 0.6 to 7 wt % (preferably 0.6 to 5 wt %) of borosilicate glass, borosilicate zinc glass or bismuth glass as an additional component.

[0111] The borosilicate glass generally indicates glass containing B₂O₃ and SiO₂, the borosilicate zinc glass generally indicates glass containing B₂O₃, SiO₂ and ZnO, and the bismuth glass generally indicates glass containing Bi₂O₃. In the definitions of these glasses, the above components do not need to be main components.

[0112] These additional glass components may be used solely or in admixture of two or three. When they are used in admixture of two or three, the total wt % of the mixture should be within the above range. By the addition of such glass, an increase in electric resistivity (increasing electric resistivity) or a decrease in dielectric constant (decreasing a dielectric constant) can be achieved. Therefore, by the addition of the glass specified by the present invention, an electric resistivity of at least 1×10⁵ Ω·m which is required for, for example, a multilayer component material as a high-frequency circuit component.

[0113] Further, by the addition of the glass specified by the present invention, the effect of decreasing a dielectric constant is also exhibited, and when the sintered body of the present invention is used as a high-frequency component, a high impedance can be attained at high frequencies and the frequency band for the impedance can be widened. Further, the above glasses must be added in the form of glass. After firing, the glass component used remains in the sintered body regardless of whether the component maintains the glass form.

[0114] Of these glasses, borosilicate zinc glass and borosilicate glass are particularly preferable for achieving high resistivity and a low dielectric constant more effectively. Further, when the above glasses are added in the same amount, bismuth glass is particularly preferable from the viewpoint that the temperature at which a relative density of at least 90% can be attained can be lowered.

[0115] As for the contents of the above main components, when the content of CoO is lower than 3 mol %, for example, the inconvenience that permeability at 2 GHz decreases (for example, to a value less than 2.0) is liable to occur, while when the content of CoO is higher than 15 mol %, the inconvenience that permeability decreases (for example, permeability at 500 MHz becomes less than 2.5, or permeability at 2 GHz becomes less than 2.0) is liable to occur.

[0116] Further, when the content of CuO is lower than 5 mol %, the inconvenience that the calcination temperature exceeds 1,000° C. is liable to occur, while when the content of CuO is higher than 17 mol %, the inconvenience that permeability at 2 GHz decreases is liable to occur.

[0117] Further, when the content of Fe₂O₃ is lower than 57 mol % or higher than 61 mol %, the inconvenience that permeability decreases is liable to occur.

[0118] As for the content of the above additional component, when the content of the above specified glass is lower than 0.6 wt %, the inconvenience that at least 90% of theoretical density cannot be obtained by firing at a temperature of not higher than 1,000° C. is liable to occur, while when the content of the above glass is higher than 7 wt %, the inconvenience that permeability decreases is liable to occur.

[0119] The addition of such an additional glass component, particularly together with the inclusion of the above CuO, markedly accomplishes low-temperature sintering. When the firing temperature is lowered, an electrode-incorporated closed magnetic circuit component can be produced easily by firing the sintered body with a low-melting-point electrode material such as Ag which is inexpensive and has a low electrical resistance incorporated therein. The thus-produced component is used in a high-frequency component (high-frequency circuit component) such as an inductor which is compact and has a high Q value or a noise filter which is compact and exhibits a high impedance at a particular frequency in a high-frequency band.

[0120] When ZnO is contained in an amount of 0 to 15 wt % (the content of ZnO would never be 0) as the MO, permeability can be significantly improved, and a particularly preferable effect is given to the attainment of a high impedance and broadening of the frequency band for the impedance when a high-frequency circuit component is prepared. Meanwhile, when NiO or MgO is contained in an amount of 0 to 15 wt % (the content of NiO or MgO would never be 0) as the MO, permeability is improved and a resonance frequency is increased. Therefore, as a high-frequency circuit component, the sintered body of the present invention exhibits a particularly preferable effect on controlling a high impedance and the band of the impedance.

[0121] In addition, at least 80%, particularly preferably at least 90%, of the sintered magnetic oxide in the present invention is constituted of a Y-type hexagonal ferrite. The unit “%” as used herein is calculated from the ratio of main peaks of X-ray diffraction intensity.

[0122] When the sintered magnetic oxide is compact sintered together with a low-melting-point metal such as silver (Ag), the firing temperature is lowered. Therefore, the Y-type hexagonal ferrite must be produced in a proportion of at least 80% at the time of calcination so that the proportion of the Y-type hexagonal ferrite after sintering should be at least 80%. Although varying depending on the composition, the decompositions of BaFe₁₂O₁₉ and BaFe₂O₄ start about 850° C. and the production of the Y-type hexagonal ferrite starts. However, when the decompositions of BaFe₁₂O₁₉ and BaFe₂O₄ do not proceed sufficiently, the production of the Y-type hexagonal ferrite does not proceed. Therefore, to have at least 80% of the Y-type hexagonal ferrite, the calcination temperature must be at least 850° C., particularly 850 to 1,000° C. Further, CuO must be contained in an amount of 5.5 to 17 mol %. When the calcination temperature is lower than 850° C. or a predetermined amount of CuO is not contained, it is difficult to produce the Y-type hexagonal ferrite in a proportion of higher than 80%. Meanwhile, when the calcination temperature is much higher than 1,000° C., fine milled powders cannot be obtained. The preparation of the fine milled powders is an extremely important technique in low-temperature firing.

[0123] From these standpoints, to achieve a high yield of the Y-type hexagonal ferrite at calcination temperatures of 850 to 1,000° C. as described above, CuO as a main component must be preferably contained in an amount of 5.5 to 17 mol %.

[0124] The sintered body of the present invention is used as a high-frequency circuit component having the structure that a conductive body is embedded in the sintered body, such as an impeder or an inductor.

[0125] The present invention will be described in more detail with reference to Examples hereinafter.

EXPERIMENT 4-I Preparations of Example Samples and Comparative Example Samples

[0126] Each material was weighed so that the compositions of ferrites after sintering should become those shown in the following Table 5, and the materials were wet-blended in a steel ball mill for 15 hours. Then, these mixed powders were calcined in the air at the temperatures shown in Table 5 for 2 hours. Then, after predetermined amounts of the predetermined glasses as an additional component were added as shown in Table 5, the calcined materials were milled in a steel ball mill for 15 hours.

[0127] The thus-obtained hexagonal ferrite powders were granulated and formed into desired shapes at a pressure of 100 MPa.

[0128] These green compacts were sintered at the temperatures shown in Table 5 for 2 hours. The compositions of the sintered hexagonal ferrites are as shown in the following Table 5. These samples were measured for magnetic permeabilities at frequencies of 500 MHz and 2 GHz at 25° C., electric resistivity and a dielectric constant, and the results of the measurements are shown in Table 6.

[0129] The target permeability at a frequency of 500 MHz is a value of at least 2.5, and the target permeability at a frequency of 2 GHz is a value of at least 2.0. Further, the target electric resistivity is a value of 1×10⁵ Ω·m. The lower the dielectric constant, the better it is. In this regard, it has been found from the experiment results to be described later that when the electric resistivity is higher than 1×10⁵ Ω·m, the dielectric constant exhibits a low value of 30 or smaller.

[0130] In addition, the proportion of a Y-type hexagonal ferrite was calculated from the ratio of intensities of X-ray diffraction peaks using the milled powders of the sintered body. TABLE 5 Additional Component (wt %) Boro- Boro- Calcination Firing Proportion Main Components (mol %) Bismuth silicate silicate Temperature Temperature of Y-Type Sample No. Fe₂O₃ CoO CuO ZnO NiO MgO BaO SrO Glass Glass Zinc Glass (° C.) (° C.) (%) Example 60 10 5.5 5 — — 19.5 — 5 — — 1000 930 95 4-I-1 Example 60 5 5.5 10 — — 19.5 — 5 — — 1000 930 95 4-I-2 Example 60 3 5.5 15 — — 16.5 — 5 — — 1000 930 95 4-I-3 Example 60 10 5.5 — 5 — 19.5 — 5 — — 1000 930 95 4-I-4 Example 60 5 5.5 — 10 — 19.5 — 5 — — 1000 930 95 4-I-5 Example 60 3 5.5 — 15 — 16.5 10 5 — — 1000 930 95 4-I-6 Example 60 10 5.5 — — 5 19.5 — 5 — — 1000 930 95 4-I-7 Example 60 5 5.5 — — 10 19.5 — 5 — — 1000 930 95 4-I-8 Example 60 3 5.5 — — 15 16.5 — 5 — — 1000 930 95 4-I-9 Example 60 14 5.5 1 — — 19.5 — 5 — — 1000 930 95 4-I-10 Example 60 14 5.5 — 1 — 19.5 — 5 — — 1000 930 95 4-I-11 Example 60 14 5.5 — — 1 19.5 — 5 — — 1000 930 95 4-I-12 Comparative 60 15 5 — — — 20 — 5 — — 1000 930 95 Example 4-I-1 Comparative 60 3 5 20 — — 12 — 5 — — 1000 930 95 Example 4-I-2 Comparative 60 3 5 — 20 — 12 — 5 — — 1000 930 95 Example 4-I-3 Comparative 60 3 5 — — 20 12 — 5 — — 1000 930 95 Example 4-I-4 Example 60 5 10 5 — — 20 — 5 — — 900 930 95 4-I-13 Comparative 60 5 10 5 — — 20 — 5 — — 850 930 46 Example 4-I-5 Comparative 60 5 10 5 — — 20 — 5 — — 800 930 0 Example 4-I-6 Example 60 5 10 5 — — 20 — 5 — — 850 930 90 4-I-14 Example 57 15 5.5 5 — — 17.5 — 5 — — 1000 930 95 4-I-15 Example 61 10 5.5 5 — — 18.5 — 5 — — 1000 930 95 4-I-16 Example 60 3 12 5 — — 20 — 5 — — 1000 930 95 4-I-17 Example 57 3 17 5 — — 18 — 5 — — 1000 930 95 4-I-18 Example 60 5 10 5 — — 10 10 5 — — 1000 930 95 4-I-19 Comparative 60 5 10 5 — — 20 — 0.3 — — 1000 930 95 Example 4-I-7 Example 60 5 10 5 — — 20 — 0.6 — — 1000 930 95 4-I-20 Example 60 5 10 5 — — 20 — 7 — — 1000 930 95 4-I-21 Comparative 60 5 10 5 — — 20 — 10 — — 1000 930 95 Example 4-I-8 Comparative 60 5 10 5 — — 20 — — 0.3 — 1000 930 95 Example 4-I-9 Example 60 5 10 5 — — 20 — — 0.6 — 1000 930 95 4-I-22 Example 60 5 10 5 — — 20 — — 5 — 1000 930 95 4-I-23 Example 60 5 10 5 — — 20 — — 7 — 1000 930 95 4-I-24 Comparative 60 5 10 5 — — 20 — — 10 — 1000 930 95 Example 4-I-10 Comparative 60 5 10 5 — — 20 — — — 0.3 1000 930 95 Example 4-I-11 Example 60 5 10 5 — — 20 — — — 0.6 1000 930 95 4-I-25 Example 60 5 10 5 — — 20 — — — 5 1000 930 95 4-I-26 Example 60 5 10 5 — — 20 — — — 7 1000 930 95 4-I-27 Comparative 60 5 10 5 — — 20 — — — 10 1000 930 95 Example 4-I-12

[0131] TABLE 6 Electric Permeability Resistivity Dielectric Sample No. 500 MHz 2 GHz (Ω · m) Constant Example 4-I-1 3.4 3.7 1 × 10⁶ 27 Example 4-I-2 5.1 4.2 1 × 10⁶ 27 Example 4-I-3 10.1  2.2 1 × 10⁶ 27 Example 4-I-4 2.7 2.3 1 × 10⁶ 27 Example 4-I-5 3.3 2.6 1 × 10⁶ 27 Example 4-I-6 5.8 2.0 1 × 10⁶ 27 Example 4-I-7 2.6 2.2 1 × 10⁶ 27 Example 4-I-8 3.2 2.5 1 × 10⁶ 27 Example 4-I-9 6.2 2.0 1 × 10⁶ 27 Example 4-I-10 2.7 2.7 1 × 10⁶ 27 Example 4-I-11 2.5 2.2 1 × 10⁶ 27 Example 4-I-12 2.6 2.1 1 × 10⁶ 27 Comparative 2.1 2.1 1 × 10⁶ 27 Example 4-I-1 Comparative 8.1 0.8 1 × 10⁶ 27 Example 4-I-2 Comparative 5.8 0.8 1 × 10⁶ 27 Example 4-I-3 Comparative 6.2 0.6 1 × 10⁶ 27 Example 4-I-4 Example 4-I-13 3.8 3.8 1 × 10⁶ 28 Comparative 2.6 1.8 1 × 10⁶ 28 Example 4-I-5 Comparative 1.8 1.8 1 × 10⁶ 28 Example 4-I-6 Example 4-I-14 3.8 3.8 1 × 10⁶ 27 Example 4-I-15 2.5 2.5 1 × 10⁶ 27 Example 4-I-16 3.0 3.0 1 × 10⁶ 27 Example 4-I-17 3.5 3.3 9 × 10⁵ 28 Example 4-I-18 3.0 2.9 9 × 10⁵ 29 Example 4-I-19 3.9 3.9 1 × 10⁶ 27 Camparative 3.4 3.4 5 × 10⁴ 35 Example 4-I-7 Example 4-I-20 3.7 3.7 3 × 10⁵ 29 Example 4-I-21 3.8 3.8 2 × 10⁶ 27 Comparative 3.0 1.9 3 × 10⁶ 27 Example 4-I-8 Comparative 2.9 2.9 8 × 10⁴ 32 Example 4-I-9 Example 4-I-22 3.2 3.2 3 × 10⁵ 29 Example 4-I-23 3.4 3.4 3 × 10⁶ 25 Example 4-I-24 3.4 3.4 9 × 10⁶ 25 Comparative 2.5 1.8 2 × 10⁷ 25 Example 4-I-10 Comparative 2.9 2.9 8 × 10⁴ 31 Example 4-I-11 Example 4-I-25 3.5 3.5 2 × 10⁵ 29 Example 4-I-26 3.6 3.6 6 × 10⁶ 27 Example 4-I-27 3.6 3.6 3 × 10⁷ 27 Comparative 2.7 1.9 5 × 10⁷ 27 Example 4-I-12

EXPERIMENT 4-II

[0132] A variety of samples were prepared by varying the types and amounts of the additional components to be added to the main components of Example 4-I-2 of the above Experiment 4-I as shown in the following Table 7. These samples were measured for the temperature at which a relative density of at least 90% (based on a theoretical density of 100).

[0133] The results are shown in the following Table 7. TABLE 7 Additional Amount of Glass Added Components 0.6 wt % 1 wt % 3 wt % 5 wt % 7 wt % Borosilicate Glass 1000° C. 1000° C. 950° C. 950° C. 900° C. Borosilicate Zinc 1000° C. 1000° C. 950° C. 950° C. 900° C. Glass Bismuth Glass 1000° C.  950° C. 900° C. 900° C. 900° C.

EXPERIMENT 4-III

[0134] Then, an impeder was prepared using the magnetic body of the present invention. That is, each material was weighed so that the composition after sintering should become the composition of the main components of the Example 4-I-2 in the above Table 5, and the materials were wet-blended in a steel ball mill for 15 hours. Then, these mixed powders were calcined in the air at 950° C. for 2 hours. Then, after 5 wt % of bismuth glass was added as an additional component, the calcined powders were milled in a steel ball mill for 15 hours.

[0135] An organic binder was mixed into the calcined powders, and the paste was formed into a uniform green sheet by a doctor blade process.

[0136] For comparison, another green sheet was prepared using NiCuZn-based spinel ferrite powders (NiO=45 mol %, CuO=5 mol %, ZnO=1.5 mol %, Fe₂O₃=48 mol %, CoO=0.5 mol %).

[0137] Meanwhile, a conductive paste containing silver was prepared, and a coil was stacked in a spiral form on the above green sheet. A pressure was applied in the thickness direction to crimp the coil onto the sheet, thereby preparing a stacked green sheet having the electrode sandwiched between the magnetic bodies. In this way the prepared green chip was sintered at 930° C. for 2 hours. The silver paste was applied to the sides of the internal conductor of the obtained sintered body to bake external electrodes thereto, thereby obtaining an impeder (high-frequency circuit component) whose schematic constitution is shown in FIG. 1. FIG. 1 shows the impeder schematically for the purpose of facilitating understanding of the internal structure thereof. In FIG. 1, reference numeral 11 denotes an inner conductor (Ag coil), reference numeral 10 terminal conductors, and reference numeral 20 a ferrite.

[0138] When the impedance and permeability of the obtained impeder were measured at a frequency of 2 GHz, the magnetic body of the present invention exhibited an extremely excellent impedance of 236 Ω (permeability: 4.2). On the other hand, the impedance of the conventional NiCuZn ferrite was 135 Ω (permeability: 1.2).

[0139] The effect of the fourth invention group of the present invention is obvious from the above result. That is, the present invention is a sintered body at least 80% of which is constituted of a Y-type hexagonal ferrite, wherein the sintered body contains, as main components, a cobalt oxide in an amount of 3 to 15 mo l% in terms of CoO, a copper oxide in an amount of 5 to 17 mol % in terms of CuO, an iron oxide in an amount of 57 to 61 mol % in terms of Fe₂O₃, 0 to 15 wt % of MO (MO is at least one of NiO, ZnO or MgO, the content of MO would never be 0), and AO (AO is at least one of BaO or SrO) as the balance, and also contains, as an additional component, 0.6 to 7 wt % of borosilicate glass, borosilicate zinc glass or bismuth glass. Thus, a sintered body which can be calcined at a temperature of not higher than 1,000° C., particularly about 900° C., has high permeability in a high-frequency band, has electric resistivity and a low dielectric constant and contains a Y-type hexagonal ferrite as a main ferrite component and a high-frequency circuit component using the sintered body, can be provided.

INDUSTRIAL APPLICABLITY

[0140] The sintered body in the present invention is used as a high-frequency circuit component having the structure that a conductive body is embedded in the sintered body, such as an impeder or an inductor. 

1. A sintered body at least 80% of which is constituted of a Y-type hexagonal ferrite, the sintered body containing, as main components, a cobalt oxide in an amount of 3 to 15 mol % in terms of CoO, a copper oxide in an amount of 5.5 to 17 mol % in terms of CuO, an iron oxide in an amount of 57 to 61 mol % in terms of Fe₂O₃, and AO (AO is at least one of BaO or SrO) as the balance, and also containing 0.5 to 7 wt % of bismuth oxide (Bi₂O₃) as an additional component.
 2. The sintered body of claim 1, wherein the calcination temperature in the production of the sintered body is in a range of 850 to 1,000° C.
 3. A high-frequency circuit component having the structure that a conductive body is embedded in a sintered body, wherein at least 80% of the sintered body is constituted of a Y-type hexagonal ferrite, and the sintered body contains, as main components, a cobalt oxide in an amount of 3 to 15 mol % in terms of CoO, a copper oxide in an amount of 5.5 to 17 mol % in terms of CuO, an iron oxide in an amount of 57 to 61 mol % in terms of Fe₂O₃, and AO (AO is at least one of BaO or SrO) as the balance, and also contains 0.5 to 7 wt % of bismuth oxide (Bi₂O₃) as an additional component.
 4. The component of claim 3, wherein the calcination temperature in the production of the sintered body is in a range of 850 to 1,000° C.
 5. The component of claim 3, wherein the conductive body contains silver (Ag) as a main component.
 6. A sintered body at least 80% of which is constituted of a Y-type hexagonal ferrite, the sintered body containing, as main components, a cobalt oxide in an amount of 3 to 15 mol % in terms of CoO, a copper oxide in an amount of 5 to 17 mol % in terms of CuO, an iron oxide in an amount of 57 to 61 mol % in terms of Fe₂O₃, and AO (AO is at least one of BaO or SrO) as the balance, and also containing 0.6 to 7 wt % of borosilicate glass, borosilicate zinc glass or bismuth glass as an additional component.
 7. The sintered body of claim 6, wherein the calcination temperature in the production of the sintered body is 850 to 1,000° C.
 8. A high-frequency circuit component having the structure that a conductive body is embedded in a sintered body, wherein at least 80% of the sintered body is constituted of a Y-type hexagonal ferrite, and the sintered body contains, as main components, a cobalt oxide in an amount of 3 to 15 mol % in terms of CoO, a copper oxide in an amount of 5 to 17 mol % in terms of CuO, an iron oxide in an amount of 57 to 61 mol % in terms of Fe₂O₃, and AO (AO is at least one of BaO or SrO) as the balance, and also contains 0.6 to 7 wt % of borosilicate glass, borosilicate zinc glass or bismuth glass as an additional component.
 9. The component of claim 8, wherein the calcination temperature in the production of the sintered body is in a range of 850 to 1,000° C.
 10. The component of claim 8, wherein the conductive body contains silver (Ag) as a main component.
 11. A sintered body at least 80% of which is constituted of a Y-type hexagonal ferrite, the sintered body containing, as main components, a cobalt oxide in an amount of 3 to 15 mol % in terms of CoO, a copper oxide in an amount of 5 to 17 mol % in terms of CuO, an iron oxide in an amount of 57 to 61 mol % in terms of Fe₂O₃, 0 to 15 wt % of MO (MO is at least one of NiO, ZnO or MgO, the content of MO would never be 0), and AO (AO is at least one of BaO or SrO) as the balance, and also containing 0.5 to 7 wt % of bismuth oxide (Bi₂O₃) as an additional component.
 12. The sintered body of claim 11, wherein the calcination temperature in the production of the sintered body is in a range of 850 to 1,000° C.
 13. A high-frequency circuit component having the structure that a conductive body is embedded in a sintered body, wherein at least 80% of the sintered body is constituted of a Y-type hexagonal ferrite, and the sintered body contains, as main components, a cobalt oxide in an amount of 3 to 15 mol % in terms of CoO, a copper oxide in an amount of 5 to 17 mol % in terms of CuO, an iron oxide in an amount of 57 to 61 mol % in terms of Fe₂O₃, 0 to 15 wt % of MO (MO is at least one of NiO, ZnO or MgO, the content of MO would never be 0), and AO (AO is at least one of BaO or SrO) as the balance, and also contains 0.5 to 7 wt % of bismuth oxide (Bi₂O₃) as an additional component.
 14. The component of claim 13, wherein the calcination temperature in the production of the sintered body is in a range of 850 to 1,000° C.
 15. The component of claim 13, wherein the conductive body contains silver (Ag) as a main component.
 16. A sintered body at least 80% of which is constituted of a Y-type hexagonal ferrite, the sintered body containing, as main components, a cobalt oxide in an amount of 3 to 15 mol % in terms of CoO, a copper oxide in an amount of 5 to 17 mol % in terms of CuO, an iron oxide in an amount of 57 to 61 mol % in terms of Fe₂O₃, 0 to 15 wt % of MO (MO is at least one of NiO, ZnO or MgO, the content of MO would never be 0), and AO (AO is at least one of BaO or SrO) as the balance, and also containing 0.6 to 7 wt % of borosilicate glass, borosilicate zinc glass or bismuth glass as an additional component.
 17. The sintered body of claim 16, wherein the calcination temperature in the production of the sintered body is in a range of 850 to 1,000° C.
 18. A high-frequency circuit component having the structure that a conductive body is embedded in a sintered body, wherein the sintered body contains, as main components, a cobalt oxide in an amount of 3 to 15 mol % in terms of CoO, a copper oxide in an amount of 5 to 17 mol % in terms of CuO, an iron oxide in an amount of 57 to 61 mol % in terms of Fe₂O₃, 0 to 15 wt % of MO (MO is at least one of NiO, ZnO or MgO, the content of MO would never be 0), and AO (AO is at least one of BaO or SrO) as the balance, and also contains 0.6 to 7 wt % of borosilicate glass, borosilicate zinc glass or bismuth glass as an additional component.
 19. The component of claim 18, wherein the calcination temperature in the production of the sintered body is in a range of 850 to 1,000° C.
 20. The component of claim 18, wherein the conductive body contains silver (Ag) as a main component. 